Catalyst for epoxidation reactions

ABSTRACT

The present invention relates to the manufacture of solid materials or shaped bodies containing at least one zeolite and being at least partly crystalline. Furthermore, the present invention relates to the solid materials or shaped bodies as such and to the use of these materials for reactions of compounds having at least one C—C double bond with at least one hydroperoxide. Specifically, the present invention relates to a process for the manufacture of a solid material containing at least one zeolite and being at least partly crystalline, wherein the synthesis of the said solid material involves at least one partial step of contacting at least one transition metal oxide source with at least one epoxide or hydrolysate thereof prior to or during the at least partial crystallization of said solid material.

The present invention relates to the manufacture of solid materials or shaped bodies containing at least one zeolite and being at least partly crystalline. Furthermore, the present invention relates to the solid materials or shaped bodies as such and to the use of these materials for reactions of compounds having at least one C—C double bond with at least one hydroperoxide. Specifically, the present invention relates to a process for the manufacture of a solid material containing at least one zeolite and being at least partly crystalline, wherein the synthesis of the said solid material involves at least one partial step of contacting at least one transition metal oxide source with at least one epoxide or hydrolysate thereof prior to or during the at least partial crystallization of said solid material.

The synthesis of solid materials containing at least Si and Ti, in particular of titanium zeolithes used for applications in catalysis, is of particular commercial importance and has resulted in a large body of prior art. By way of example, U.S. Pat. No. 4,666,692 and U.S. Pat. No. 4,410,501 are cited in the general context of the manufacture of titanium silicalites.

An integrated process for producing solid materials containing Si and Ti and shaped bodies produced therefrom is described, e.g. in WO 98/55229.

The scientific publication “Studies of the synthesis of titanium silicalite, TS-1” from A. Thangaraj et al. [Zeolites 12 (1992) 943 ff] relates to a procedure to obtain TS-1, wherein the precipitation of titanium oxide during the hydrolysis of the alkoxides in the synthesis mixture is minimized or avoided by adding, in a separate step, isopropyl alcohol to the titanium source. Not only is it found that the amount of metal oxide precipitation indeed decreases, but also that more Ti is built into the silicalite framework. However, said publication is silent as to the use of other compounds to be added to a transition metal oxide source and is silent as to the effect such treatment has on the catalyst actually used in a chemical reaction, e.g. an epoxidation reaction.

Referring to said scientific publication, US application 2001/0041162 A1 describes the use of alcohols having a pK_(a) value lower than that of water, more specifically the use of 2-ethoxyethanol, in order to avoid precipitation of metal oxides such as anatase, from the synthesis solution. As a result it is found that indeed the molar fraction of precipitated Ti in anatase form is significantly reduced. However, no significant effect on important performance characteristics of the catalyst actually used for epoxidation reactions were identified, in particular on epoxide selectivity.

The object of the present invention is to provide a catalyst, and a process for the manufacture thereof which results in improved performance characteristics of the catalyst based on zeolite materials, in particular with respect to selectivity and activity, over the catalysts of the prior art.

Surprisingly, it has been found that by adding the epoxide that is the product of the desired catalyzed epoxidation reaction, or a hydrolysate thereof, to the transition metal oxide source, the performance characteristics of the catalyst obtained from the synthesis mixture comprising the transition metal oxide source treated according to the inventive process, is improved over a corresponding catalyst which had not been subjected to the inventive step of adding an epoxide or hydrolysate thereof to the transition metal oxide source.

The catalytic material (solid material or shaped body) obtainable by the inventive process of adding an epoxide or hydrolysate thereof can be used for any catalytic reaction, preferably for a catalytic reaction in which it improves at least one reaction parameter or catalyst performance characteristic, such as selectivity, yield, activity, over the respective values obtained using catalytic material that has not been subjected to the inventive treatment of adding an epoxide or hydrolysate thereof to the transition metal oxide source.

Preferably, the catalytic material obtainable by the inventive process is used in reactions of compounds containing at least one C—C-double bond with at least one hydroperoxide, i.e. in epoxidation reactions.

In the following, a glossary of the most important expressions used in the context of the present invention are defined.

A “synthesis mixture” as used in the context of the present invention pertains to any mixture which yields, by means of crystallization, a mixture containing a solid material which is at least partially crystalline, and a fluid material. Preferably, the synthesis mixture contains at least a Si source (Si precursor), a transition metal oxide source (transition metal precursor) and a mineralizing and/or structure forming agent. In particular, reference is made to all synthesis mixtures known to the expert in the field of zeolite preparation, particularly to synthesis mixtures used for the hydrothermal treatment of gels. The synthesis mixture may be a sol, gel, solution, or a suspension. The synthesis mixture may be obtained by mixing two or more separate solutions.

“Zeolites” as used in the context of the present invention are crystalline alumosilicates with well-ordered channel or cage structures containing micropores. The expression “micropore” as used in the context of the present invention corresponds to the definition given in “Pure Applied Chemistry”, Vol. 45, p. 71 ff., in particular p. 79 (1976). According to this definition, micropores are pores with a pore diameter of less than 2 nm. The network of these zeolites is made of SiO₄ and AlO₄-tetrahedra that are bridged via shared oxygen bonds. An overview of the known structures can be found in, e.g., W. M. Meier und D. H. Olson in “Atlas of Zeolite Structure Types”, Elsevier, 4^(th) Ed., London 1996. In addition to micropores, solid materials or shaped bodies according to the invention may contain mesopores and/or macropores as well.

“Solid materials” as obtained, for example, after the crystallization of the synthesis mixture, are to be understood in the context of the present invention as any known material which displays at least the following properties: (i) it contains at least one zeolite material and (ii) is different from the synthesis mixture described before in the sense that a separation of said solid material from its mother liquor is possible and/or concentrating of the solid material by, e.g., ultra-filtration is possible. Typically, the solid material prevails as particles suspended in the mother liquor.

A “mother liquor” in the context of the present invention is any liquid phase that may contain an unlimited number of substances dissolved therein, however in itself is not a solid material. In particular, the mother liquor may contain adjuvants dissolved therein. In the sense of the present invention, a mother liquor can only occur after step (I) of the integrated process as described above. Typically, a mother liquor is the liquid phase in which the solid material is suspended in the form of particles. Said mixture (I) is then subjected to step (II) of separating and/or concentrating of the solid material in mixture (I).

The term “epoxide” as used in the context of the present invention refers to any compound with at least two adjacent carbon atoms, wherein at least those two carbon atoms are, at least partly, chemically bound to one mutual oxygen atom. By way of example, propylene oxide is mentioned. A “hydrolysate” of an epoxide is the product of the reaction of the epoxide with any compound leading to hydrolysis, e.g. water. By way of example, propylene glycol is mentioned as the hydrolysate of the above mentioned propylene oxide.

Step (II) of the present invention relates to concentrating and/or separating of the solid material in the mother liquor and/or from the mother liquor, wherein the mixture (I) containing the solid material is obtained from step (I). The term “concentrating and/or separating is to be understood in the context of the present invention as any step that at least results in that, at the end of step (II), the solid material content in the mixture is increased and/or the solid material is separated partly or entirely from the mother liquor.

The complete “separation” of the solid material from the mixture (the suspension) is explicitly contained in the definition of “concentrating” as a specific case. Such methods of separating and/or concentrating include, but are not limited to, spray-drying or ultra-filtration and will be described in more detail below. The terms “filtration”, “ultra-filtration”, and “spray-drying” as well as other methods of concentrating and/or separating the solid material from the mother liquor are described in detail in DE 102 32 406.9, the respective content of which is hereby incorporated by reference.

A “shaped body” as used in the context of the present invention is to be understood to be any three-dimensional entity which can be obtained by any of the shaping steps (S) mentioned below. The shaped body is obtained in a typical manner by means of compacting of the solid material described above. Said solid material may originate from steps (II) and/or (III), using optional step of calcining (C).

The expressions “granulating” and “agglomerating” as used in the context of the present invention are to be seen as synonymous and describe, respectively, any conceivable process that can be used to increase the diameter of the particles obtained from step (II). Said increase of the particle diameter can be achieved by baking the particles together or by growing on the particles layer by layer. The process of granulating thereby includes, but is not limited to, processes taking advantage of the phenomenon of wetting of the particles by at least one liquid. Furthermore, binding materials may be added to the mixture in order to enhance or enable the agglomerating and/or granulating of the particles.

A “binding material” as used in the context of the present invention is to be understood to be any material that enables a physical, chemical, or physical-chemical bond between the substances constituting the particle. Such binding materials may be used in the step (S) of shaping or forming the solid material into a shaped body as well. Reference is made to the description of binding materials in that context.

The inventive treatment of adding an epoxide or hydrolysate thereof to the transition metal oxide source is preferably part of an integrated process, namely an integrated process producing a mechanically stable solid material or a shaped body containing at least one zeolite material. Schematically, such an integrated process can be characterized by the following steps

(I) at least partial crystallization of at least one solid material containing at least one zeolite out of a synthesis mixture, resulting in mixture (I) containing at least said solid material and a mother liquor;

(II) separating and/or concentrating of the solid material from mixture (I);

(W) bringing the solid material from step (II) in contact with a composition containing water;

(III) agglomerating, or granulating, or agglomerating and granulating of the solid material from step (W);

wherein steps (W) and (III) are optional. Step (II) may additionally include the drying and/or washing of the solid material, possibly also in several iterations.

Additionally and/or optionally, the following steps may be part of the integrated process as well:

(S) shaping of the solid material into shaped bodies subsequent to steps (W) or (III);

(C) Calcining of the solid material and/or the shaped body at temperatures higher than 400° C.;

wherein the step (C) of calcining may be performed at least once after at least one of the following steps of the integrated process: (II), (W), or (III).

In a preferred embodiment, step (W) is performed after step (S) of shaping the solid material.

In the present application, the inventive solid material containing at least one zeolite material or the shaped body obtainable therefrom is discussed in the context of applications in the field of catalysis. This, however, cannot be construed as a limitation of the use of the solid material and/or the shaped body to the field of catalysis. The explicit discussion of examples in the field of catalysis is illustrative only. The inventive material may be used in other fields as well.

In the following, the individual steps of the integrated process for producing a solid material and/or shaped body are summarized, wherein the solid material and/or the shaped body contain(s) at least one zeolite material and is/are at least partially crystalline. Of particular importance is step (D) containing the inventive partial step (Ib).

Step I: (Partial) Crystallization of the Synthesis Mixture

According to the present invention, step (I) of the at least partial crystallization of at least one solid material containing at least one zeolite out of a synthesis mixture, resulting in mixture (I) containing at least said solid material and a mother liquor comprises at least the following partial steps

-   -   (Ia) mixing of at least one hydrolyzable silicon source with a         mineralizing and/or structuring agent and water;     -   (Ib) mixing of at least one transition metal oxide source with         an epoxide or a hydrolysate thereof;     -   (Ic) mixing of the mixtures from (Ia) and (Ib) so that at least         a part of the hydrolyzable compounds hydrolyzes;     -   (Id) distilling at least parts of the alcohol that has been         formed as a result of the at least partial hydrolysation of at         least part of the hydrolyzable compounds;     -   (Ie) adding water to the bottom of (Id);     -   (If) reacting of the synthesis mixture resulting from (Ie) at a         temperature elevated with respect to room temperature.

Preferably, steps (Ia) and (Ib) are performed in separate containers.

In a preferred embodiment, the hydrolyzable silicon source comprises at least one silicon oxide, the mineralizing and/or structuring agent comprises at least one tetraalkylammonium hydroxide, the transition metal oxide source comprises at least one titanate and the epoxide or hydrolysate thereof comprises at least the epoxide or the hydrolysate thereof of the reaction for which the solid material is ultimately used as a catalyst.

In a further preferred embodiment, the hydrolyzable silicon source comprises at least tetraethoxy silicate, the mineralizing and/or structuring agent comprises at least tetrapropylammonium hydroxide, the transition metal oxide source comprises at least tetrabutylorthotitanate, and the epoxide or the hydrolysate thereof comprises at least propylene oxide or propylene glycol, with propylene glycol being particularly preferred.

As far as the at least one zeolite material resulting from said synthesis step (I) is concerned, no limitations exist. Preferably, a zeolite containing titanium, zirconium, chromium, niobium, iron, bor, and/or vanadium is employed. Particularly preferably, a zeolite containing titanium is employed, wherein zeolites known to the expert in the field as “titanium silicalites” (TS) are especially preferred.

Such zeolites containing titanium, in particular those having a crystalline structure of the MFI-type as well as ways for producing them are described, for example, in WO 98/55228, WO 99/55229, WO 99/29426, WO 99/52626, EP-A 0 311 983, or EP-A 405 978. The respective content of these documents is hereby incorporated by reference. In addition to Si and Ti, said zeolite materials may contain additional elements, such as aluminum, zirconium, tin, iron, cobalt, nickel, gallium, bor, or small amounts of fluorine. It is possible that the titanium of the zeolite is partly or completely replaced by vanadium, zirconium, or niobium, or any mixture of two or more of these components.

Zeolites containing titanium and displaying a MFI-structure are known to yield a characteristic pattern in X-ray diffraction. Furthermore, these materials display a vibration band in the infrared (IR) at approximately 960 cm⁻¹. Therefore, it is possible to distinguish the zeolites containing titanium from crystalline or amorphous TiO₂-phases or from alkali metal titanates.

In a further preferred embodiment, the at least one zeolite material is selected from the following group: zeolites containing at least one of the following elements: titanium, germanium, tellurium, vanadium, chromium, niobium, zirconium, particularly those having a pentasil zeolite structure, in particular the structural types that can be, via X-ray diffraction, assigned to the structure types of ABW-, ACO-, AEI-, AEL-, AEN-, AET-, AFG-, AFI-, AFN-, AFO-, AFR-, AFS-, AFT-, AFX-, AFY-, AHT-, ANA-, APC-, APD-, AST-, ATN-, ATO-, ATS-, ATT-, ATV-, AWO-, AWW-, BEA-, BIK-, BOG-, BPH-, BRE-, CAN-, CAS-, CFI-, CGF-, CGS-, CHA-, CHI-, CLO-, CON-, CZP-, DAC-, DDR-, DFO-, DFT-, DOH-, DON-, EAB-, EDI-, EMT-, EPI-, ERI-, ESV-, EUO-, FAU-, FER-, GIS-, GME-, GOO-, HEU-, IFR-, ISV-, ITE-, JBW-, KFI-, LAU-, LEV-, LIO-, LOS-, LOV-, LTA-, LTL-, LTN-, MAZ-, MEI-, MEL-, MEP-, MER-, MFI-, MWS-, MON-, MOR-, MSO-, MTF-, MTN-, MTT-, MTW-, MWW-, NAT-, NES-, NON-, OFF-, OSI-, PAR-, PAU-, PHI-, RHO-, RON-, RSN-, RTE-, RTH-, RUT-, SAO-, SAT-, SBE-, SBS-, SBT-, SFF-, SGT-, SOD-, STF-, STI-, STT-, TER-, THO-, TON-, TSC-, VET-, VFI-, VNI-, VSV-, WIE-, WEN-, YUG-, ZON, as well as mixed structures of at least two or more of the aforementioned structures. Furthermore, it is conceivable to use zeolites containing titanium with the structure of ITQ-4, ITQ-9, SSZ-24, TTM-1, UTD-1, CIT-1 or CIT-5. Further zeolites containing titanium are such of the structure types ZSM-48 or ZSM-12.

Zeolites containing titanium of the structure MFI, MEL or MFI/MEL mixed structures, as well as MWW, BEA or mixed structures thereof are preferred in the context of the present invention. Further preferred in the context of the present invention are these zeolite catalysts containing titanium that are referred to, in general, as “TS-1”, “TS-2” or “TS-3”, as well as zeolites containing titanium having a structure that is isomorphous to β-zeolite.

If necessary, or advantageous, additional compounds may be added. The reaction or mixing of each partial step of step (I) is performed in an open container or in a pressure-tight container (autoclave), optionally at elevated temperatures, over the course of several hours or days. Thereby, a product that is at least partly crystalline is obtained.

As far as the duration of the inventive partial step is concerned, no limitations exist, as long as the partial step results in an improved performance of the catalyst over a catalyst that had not been subjected to that partial step. As a measure for the increased performance, activity, selectivity and/or yield may be used. Increased mechanical stability or improved properties that are otherwise relevant for the process of interest can be used as well. In a preferred embodiment, the inventive partial step (Ib) consists of mixing the transition metal oxide source with the epoxide or hydroxide and stirring until the solution is transparent to the eye.

Step (II): Separating and/or Concentrating

In step (II) the solid material is separated from the mother liquor and/or is concentrated in the mother liquor. Step (II) is performed with mixture (I) from step (I). Methods of separating and/or concentrating include, but are not limited to, filtration, ultrafiltration, diafiltration, centrifuge methods, spray drying, spray granulating, etc.

This step (II) of concentrating and/or separating is preferably performed prior to step (W) of bringing the solid material in contact with a composition containing water and after the step (I) of crystallizing the solid material. The purpose of step (II) is to increase the solid content in the mixture resulting from step (I). For details of filtration and/or concentration, reference is made to DE 102 32 406.9, the respective content of which is hereby incorporated by reference.

Preferably, the solid material is concentrated first and then separated from the mother liquor by filtration. For example, the method of ultrafiltration may be used for concentrating the solid material in the retentate, while the solid material may be separated from all or parts of the mother liquor by means of conventional filtration. With respect to conventional filtration, all methods known to the expert in the art may be used such as cake filtration or methods involving a centrifuge.

In another preferred embodiment, step (II) consists of bringing an inert support body in contact with the synthesis mixture from step (I). As far as the “inert support body” is concerned, no limitations exist, as long as the inert support body does not react noticeably with the synthesis mixture or any component thereof and said inert support body is capable of accommodating, at least partly, the solid material contained in the synthesis mixture from step (I), preferably in the form of a (thin) film. Such inert support bodies may include, but are not limited to, beads or pellets made form technical ceramic materials such as alumosilicate ceramics, alkali alumosilicate ceramics, aluminum oxide based ceramics (e.g. mullit), magnesium silicates (e.g. steatit, cordierit). The use of steatit or mullit is preferred. Said inert support bodies may be porous or dense, wherein the use of dense support bodies is preferred.

Said support bodies may be brought in contact with the synthesis mixture from step (I) by means of all methods known to expert in the context of bringing a solid body in contact with a fluid medium. Spraying of the synthesis mixture onto the support bodies, dipping the support bodies into the synthesis mixture or saturating/soaking of the inert support bodies in the synthesis mixture are preferred. In case the method of bringing in contact is soaking/dipping/saturating, in a preferred embodiment, the soaked/dipped/saturated support bodies are exposed to an atmosphere with a partial pressure of the liquid medium of the synthesis mixture (e.g. water) lower than the pressure of the pure liquid, so that the liquid medium may, at least partly, evaporate.

As a result of said step of bringing inert support bodies in contact with the synthesis mixture from step (I), a (thin) film containing the solid material containing at least one zeolite and being at least partly crystalline forms on the support body and/or in the pores, if the support body is porous. The thickness of the film so formed may range from 1 μm to 1500 μm. In a preferred embodiment, the thickness of the film ranges from 5 μm to 50 μm. The result of this embodiment is referred to a “solid material” in the context of the present invention and is processed the same way the solid material obtained by spray drying or ultrafiltration.

The solid material obtained after step (II) may now be optionally subjected to at least one step of washing and to at least one step of drying of the solid material. Furthermore, after the at least one step of drying, the solid material may also be calcined at temperatures of 400° C. and higher (see description of the step (C) of calcining given below).

Step (W): Treatment of the Solid Material With a Composition Containing Water

Subsequent to step (II) of concentrating and/or separating, the solid material may be subjected to a treatment of bringing the solid material in contact with a composition containing water.

As far as the term “bringing in contact” is concerned, any method is conceivable, in which the solid material is brought in physical contact with a composition containing water. This includes, but is not limited to: forming a slurry, suspension or mixture of the solid material in or with the composition containing water, the composition being preferably in a liquid phase, spraying the solid material with the composition containing water, subjecting the solid material to the composition containing water in the form of vapor and/or steam. It is particularly preferred to form a slurry of the solid material with the composition containing water in a stirring tank.

Preferably, the same stirring tank is used for step (W) that has already been used for crystallizing the solid material out of the synthesis mixture. For additional physical contact between the solid phase and the composition containing water, any means for stirring or otherwise mechanically acting the mixture containing the solid material and the composition containing water known to the expert in this field can be employed. Other methods of mixing and/or agitating, such as ultrasound agitation, magnetic stirring and the like are conceivable as well. Preferably the slurry of the solid material is brought in contact with a composition containing water in a tank vessel with a mechanical stirring device.

As far as the composition containing water is concerned, any substance can be used that contains, at least in parts, water in any of its modifications. These modifications include the liquid phase, the solid phase, vapor, steam, super critical water. Furthermore, the water may by mixed with other substances. Preferably water is used as such in the liquid phase or as steam. If water is used in the liquid phase, deionized water is preferred. Any method to deionize water known to the expert in the art is included, such as distillation or removing of electrolytes over an ion exchanger. While not preferred, the use of water containing salt and/or of water that is acidic or basic is conceivable as well.

For specific applications, bringing the solid material in contact with an aqueous ammonia solution may be preferred. In this case, a solution of ammonia in water is preferred, wherein the content of ammonia in water, given in % by weight with respect to the total weight, ranges from 5 to 60, preferably from 10 to 30. If a composition containing water and ammonia is used, step (W) is preferably carried out at pressures elevated with respect to ambient pressure and not exceeding several hundred bar.

As far as the ratio between the amount of solid material and the composition containing water is concerned, no principal limitations exist, save for the fact that the mixture or slurry should have viscous or hydraulic properties conducive to mechanical stirring.

Furthermore, it is preferred that the treatment of bringing the solid material in contact with a composition containing water is performed at a temperature elevated with respect to room temperature. Temperatures between room temperature and 750° C. are preferred. Temperatures between 100° C. and 250° C. are particularly preferred, while temperatures between 120° C. and 175° C. are further preferred.

The treatment (W) of the solid material with a composition containing water can be performed with any type of solid material. The solid material may be the material obtained from step (II) without drying or calcining. However, it is preferred that the solid material from step (II) has been dried and/or calcined before the treatment. It is further preferred that the solid material has been washed, dried and optionally calcined prior to step (W). It is further preferred that the solid material has been obtained by spray granulation and/or ultrafiltration (in conjunction with conventional filtering).

After the optional step (W) has been performed, i.e. after the solid material has been brought into contact with the composition containing water, the composition containing water may be removed from the solid material and/or the solid material may be concentrated in the composition containing water. To achieve this end, step (II) may be repeated. This is, the mixture containing the solid material and composition containing water may be subjected to, e.g., spray/drying, ultrafiltration, or ultrafiltration in conjunction with conventional filtration. It may be only subjected to conventional filtration as well.

Step (III): Agglomerating/Granulating

Subsequent to step (W), the solid particles can be increased in their size using any method of agglomerating and/or granulating known to the expert in the field. For a list of methods used in this context, reference is made to DE 102 32 406.9, the respective content of which is hereby incorporated by reference.

Post-Treatment

In order to improve the catalytic performance of the final product, subsequent to step (W) or to step (III) or subsequent to both, it is optionally possible to perform at least one step of post-treatment of the material, including, but not being limited to, drying, washing, calcining, treating of the solid material with a hydrogen peroxide solution. Any combination of these steps is conceivable as well. It is also possible to treat this solid material containing at least one zeolite material with compounds containing alkali metal, in order to transform the zeolitic material from the H-form into the cationic form. The solid material obtained after step (W) or after step (III) or after any of the two steps in conjunction with any of the steps of post treatment mentioned here, can then be processed further to a shaped body, as described below.

Step (S): Shaping of the Solid Material

The starting point for the process to produce a shaped body containing at least one zeolite is either the solid material after step (II) or the solid material after step (W) or the solid material after step (III), optionally involving any of the steps of post-treatment mentioned in the preceeding paragraph. As it has been mentioned above, if the process so far has involved at least one step (W) of bringing the solid material in contact with a composition containing water, the material obtained after step (S) does not need to be subjected to a step (W). However, if the solid material so far has not been subjected to the treatment (W), the step of bringing the shaped body in contact with at least one composition containing water has to be performed after the step (S) of shaping the solid material or after said step (S) in conjunction with a step (C).

In any case, the step (S) of shaping the solid material involves at least one step of forming a three-dimensional material that contains at least one zeolite material. As far as this specific (at least one) step of shaping the solid material is concerned, reference is made to WO 98/55229 and to DE 102 32 406.9 whose respective content is incorporated into the present application by reference.

Preferably, a binding material is added to the solid material resulting from any of the steps mentioned above. Further adjuvants that may be added to the solid material prior to the step (S) include, but are not limited to, mixtures containing at least one alcohol and water, if suitable one or more organic substances increasing the viscosity, and further substances known from the prior art.

Preferably, the solid material is milled and mixed with silica sol, a dispersion of polystyrene, cellulose and polyethlylene oxide (PEO), as well as with water. Said mixture is homogenized in any type of kneading apparatus. In lieu of or in addition to kneading, any method of bringing the substances into physical contact may be used. Preferably, the mass obtained by this method shows plastic flow. The shaped body can then be obtained from this mass, e.g., by means of molding, in particular extrusion molding, or by any other method of extrusion known to the expert in the field.

As far as the binding materials are concerned, in principle, every substance can be used that achieves cohesion between the particles that is increased over the cohesion achieved without the presence of the binding material. Preferred binding materials are selected from the group consisting of hydrated silica gel, silicic acid, tetraalkoxy silicates, tetraalkoxy titanates, tetraalkoxy zirconates and a mixture of two or more of the afore-mentioned substances. Tetraalkoxy silicates such as tetramethoxy silicates, tetraethoxy silicates, tetrapropoxy silicates or tetrabutoxy silicates are preferred. Tetramethoxy silicates or tetraethoxy silicates and silica sols are particularly preferred.

Further preferred binding materials are amphiphilic substances, i.e. molecules with a polar and a non-polar part. The use of graphite is conceivable as well. As far as further binding materials are concerned, reference is made to WO 98/55229 and to DE 102 32 406.9 whose respective content is incorporated into the present application by reference.

Said binding materials can be used either alone or as a mixture of two or more thereof, or they can be used together with other materials to be used for enabling or enhancing the binding of materials containing zeolite, such as oxides of silicon, bor, phosphor, zirconium, and/or titanium. By way of example, clays are also to be mentioned.

In the process of shaping the solid material into a shaped body, up to approximately 80% by weight of binding materials with respect to the total mass of the shaped body may be used. It is preferred to use from approximately 10 to approximately 75% by weight of binding materials, while using 25% to approximately 45% is particularly preferred.

The binding material may be added to the solid material before, or during, or before and during the step (S) of shaping the solid material.

In the process to produce a shaped body, polymers may be added to create pores of a certain size, a certain volume and/or a certain size distribution. In the context of the present invention, polymers are preferred that can be dispersed, emulsified or suspended in aqueous solvents. Said at least one polymer is preferably selected from the group of polymer vinyl compounds, such as polystyrene, polyacrylates, polymethacrylates, polyolefins, polyamids, and polyesters. These polymers are removed from the shaped bodies after the process of forming and/or shaping by means of calcining the shaped body. If polymers are added, the content of polymer during the production of the shaped body amounts to from approx. 5 to approx. 90% by weight, preferably from approx. 15 to approx. 75% by weight, wherein a content ranging from 25 to 55% by weight is particularly preferred. The amounts given in weight-% refer to the amount of polymer in the solid material containing zeolite, respectively.

Furthermore, it is preferred to add a pasting agent. As far as the pasting agent is concerned, any substances known from the prior art to improve the mixing, kneading, or flow properties of the mass can be used. Preferably, organic hydrophilic polymers are used, such as cellulose, starch, polyacrylates, polymethacrylates, polyvinylalcohol, polyvinyl pyrrolidone, polyisobutene, polytetrahydrofuran. Primarily, these substances enable or improve the formation of a plastic mass during the process of kneading, forming, and/or drying by means of bridging the primary particles. Moreover, these adjuvants enable or enhance the mechanical stability of the shaped body during the steps of forming or drying.

These substances are removed from the shaped body by means of calcining after the step of shaping. Further adjuvants are described in EP-A 0 389 041, EP-A 0 200 260, and in WO 95/19222, the entire contents of which are hereby incorporated by reference.

In a preferred embodiment, after having added the binding material to the solid material containing at least one zeolite, the organic substance increasing viscosity is added and the mass is homogenized for 10 to 180 minutes in the kneading apparatus or in the extruder. The temperature applied to the mass is typically about 10° C. under the boiling point of the pasting agent. The pressure is either ambient pressure or slight over-pressure. In principle, the order of adding additional components to the solid material and the binder is not believed to be critical. The mass obtained as described above is kneaded until a plastic mass can be extruded.

In the context of the present invention, those methods for forming a shaped body from a solid material are preferred, in which the forming can be performed in commercially available extruders. Preferably, extrudates of a diameter ranging from approx. 1 to approx. 10 mm are used, particularly preferred are extrudates with diameters ranging from approx. 2 to approx. 5 mm. Extruders that can be used in the context of the steps described here are described, for example, in “Ullmann's Enzyklopaidie der Technischen Chemie”, 4^(th) Edition, Vol. 2, p. 205 ff. (1972).

In principle, all methods of shaping and forming that are known to the expert in the art can be used. Next to extrusion, other known methods are briquetting, pelleting, pressing, sintering, or roasting.

The technique of co-extruding can be employed as well. Here, two materials are co-extruded simultaneously. Preferably the aforedescribed active material (solid material according to the invention) is extruded together with an inert material, i.e. a material that does not react noticeably with the active material. Preferably, the matrix of the extruder is designed so that the active material is extruded as a layer on the inert material. Therefore, strands result whose core is made of the inert material and whose outer layer is the active solid material. In a preferred embodiment, the thickness of the active layer ranges from 1 to 1500 μm, preferably from 5 to 50 μm.

The use of binding materials or other adjuvants is in any event optional. The materials to be compacted may be dry or moist or may prevail as a slurry.

The step of shaping and/or forming can be performed at ambient pressure or at a pressure that is elevated with respect to ambient pressure, for example, in a pressure range from 1 bar to 700 bar. Furthermore, the shaping and/or forming can be performed at ambient temperature or at a temperature increased with respect to ambient temperature, e.g., a temperature which is ranging from 20° C. to approx. 300° C. If drying and/or sintering is part of the shaping and/or forming step, temperatures of up to 1500° C. are conceivable. Furthermore, the step of compacting and of forming can be performed at ambient atmosphere or in a controlled atmosphere. Controlled atmospheres include, but are not limited to, inert gas atmospheres, reducing atmospheres, or oxidizing atmospheres.

Post-Treatment of the Shaped Body

After forming and/or shaping (S) the shaped bodies, they are typically dried at temperatures ranging from approx. 30° C. to approx. 140° C. for a time interval typically ranging from 1 h to 20 h. Subsequent to this step, the shaped body is calcined at temperatures ranging from approx. 400° C. to approx. 800° C. and for a time interval ranging from approx. 3 h to approx. 10 h. Calcining can be performed at ambient pressure, preferably in air or in a mixture containing air or under inert conditions.

In another step of post-treatment, the extrudates obtained as described above may be milled and/or crushed. The milling and/or crushing preferably leads to a granulate with an average particle diameter ranging from 0.1 to approx. 5 mm. Particle diameters ranging from approx. 0.5 to 2 mm are particularly preferred.

Subsequent to the step (S), or subsequent to said step (S) in conjunction with any step of post-treatments such as (in particular) drying and calcining, the treatment of bringing the solid material, in this case a shaped body, in contact with a material containing water, i.e., the step (W) may be performed.

If the step (W) is performed at this point, i.e. after the step (S) or the steps (S) and (C) in conjunction, everything that has been disclosed before about the specific embodiments of said step of (W) is valid here as well. In a preferred embodiment, the shaped body is charged into the reactor that is used for the desired reaction, typically an epoxidation reaction, and said shaped body is subjected to the treatment with the composition containing water in the reactor. Preferably the treatment consists in exposing and/or bringing in contact of the shaped body with water steam.

In addition to the process for producing a solid material and/or a shaped body as described above, the present invention also relates to the respective material or shaped body as such.

In particular, the solid material according to the invention is obtainable by a sequence of the following steps

(I) at least partial crystallization of at least one solid material containing at least one zeolite out of a synthesis mixture, resulting in mixture (I) containing at least said solid material and a mother liquor;

(II) separating and/or concentrating of the solid material from mixture (I);

(W) bringing the solid material from step (II) in contact with a composition containing water;

(III) agglomerating, or granulating, or agglomerating and granulating of the solid material from step (W);

wherein the steps (III) and (W) are optional Step (II) may additionally include the drying and/or washing of the solid material, possibly also in several iterations.

Here, the inventive partial step (I b) is part of the above mentioned step (I):

-   -   (Ia) mixing of at least one hydrolyzable silicon source with a         mineralizing and/or structuring agent and water;     -   (Ib) mixing of at least one transition metal oxide source with         an epoxide or a hydrolysate thereof;     -   (Ic) mixing of the mixtures from (Ia) and (Ib) so that at least         a part of the hydrolyzable compounds hydrolyzes;     -   (Id) distilling at least parts of the alcohol that has been         formed as a result of the at least partial hydrolysation of at         least part of the hydrolyzable compounds;     -   (Ie) adding water to the bottom of (Id);     -   (If) reacting of the synthesis mixture resulting from (Ie) at a         temperature elevated with respect to room temperature.

Furthermore, the present invention relates to a shaped body obtained from the solid material described above. The shaped body is obtained by subjecting the solid material to a step (S) of shaping, as described in detail above, and (optionally) to a step (C) of calcining. The sequence of the steps is schematically shown below:

-   -   (I) at least partial crystallization of at least one solid         material containing at least one zeolite out of a synthesis         mixture, as described above in (Ia) to (If), resulting in         mixture (I) containing at least said solid material and a mother         liquor;     -   (II) separating and/or concentrating of the solid material in         mixture (I);     -   (III) agglomerating or granulating or agglomerating and         granulating of the solid material from step (W);     -   (S) shaping of the solid material from step (II) or (III)

Hereby, the following step (W) can optionally be performed after step (II) or after step (S) or after step (II) and after step (S):

-   -   (W) bringing the shaped body from step (S) in contact with a         composition containing water;

Finally the present invention relates to the use of the inventive materials, i.e. the solid material and/or the shaped bodies as catalysts. The materials obtainable by the inventive process or the materials obtained by the inventive process are particularly suited for catalytic reactions involving compounds with at least one C—C-double bond. Particularly preferred is the reaction of at least one compound containing at least one C—C-double bond with at least one hydrogen peroxide. These reactions are also referred to as epoxidation reactions. As far as further possible reactions are concerned for which said catalysts may be employed, reference is made to DE 102 32 406.9 the respective content of which (in particular pages 27 and 28) is hereby incorporated by reference.

EXAMPLE C1 (COMPARATIVE EXAMPLE)

In a four neck flask, 658 g of tetraethoxysilane were mixed with 20.8 g of tetraethylortho-titanate. While stirring, a solution of 340 g of tetrapropylamoniumhydroxide (40% by weight, in water) and 563 g of deionized water were added slowly thereto.

The solution was stirred at room temperature for 1 hour. Subsequently, the alcohol formed due to hydrolysis was distilled at a bottom temperature of 92° C. The bottom (915 g) was filled with water to 1600 g.

This batch was reacted in a steel autoclave at 175° C. and for 24 hours while being stirred. After the mixture had cooled down, it consisted of a white suspension. Therefrom, the solid material was filtrated, rinsed with water and dried at 120° C. for 24 hours. Subsequently, said material was calcined in air twice times for 5 hours, respectively, at a temperature of 450° C.

The yield of isolated solid material was 190 g. The content of Ti of the zeolite of MFI-structure thus obtained was 2.1% by weight.

The following test of the catalytic material as described above had been performed: In a pressure-tight glass reactor, 0.5 g of said catalyst was mixed with 45 ml of methanol. At a temperature of 0° C., 20 ml of propylene were dosed in and subsequently, by means of a pump, 18 g of hydrogen peroxide (30% by weight, in water; Merck) were metered in. After a reaction time of 5 hours, the mixture was expanded (pressure released) and the liquid phase was analyzed by means of gas chromatography. The reaction mixture contained 8.7% by weight of propylene oxide.

EXAMPLE C2

The catalyst material as described above was shaped into a shaped body according to the following procedure: 60 g of the inventive solid material as described in Example C1 were milled and mixed with the following substances: 56.5 g of silica sol (Ludox AS 40% by weight SiO₂), a total amount of 32.9 g of a polystyrene dispersion (43.5 weight % of polymer), 2.7 g of methyl cellulose (Walocel) and 0.88 g of polyethylene oxide (PEO). 20 g of water were added to the mass. Said mass was homogenized in a kneading apparatus.

However, the materials were not added at the same time. Specifically, during the process of kneading, the polystyrene dispersion was added within 5 minutes, and after 10 minutes the silica sol was added slowly. After 10 further minutes of kneading, the PEO was added and gobbled for a further 10 minutes. Subsequently, water was added in portions of 5 ml, respectively.

The paste so obtained was formed after a total of 60 minutes of kneading and at an extrusion pressure of 70 bar via an extruder having a matrix of 1.5 mm holes. This way the solid material was alternately formed into strands.

The shaped body obtained this way was dried for 4 hours at 120° C. (heating ramp of 2 K per minute). Finally, the shaped body was calcined at 490° C. for 4 hours (heating ramp 1 K per minute). The atmosphere was air. The yield was 65.24 g. The content of titanium of the shaped body produced this way was 1.4% by weight.

Said shaped body was subjected to a long term test for selectivity: 13.5 g of the shaped bodies were loaded into a tube reactor (1.3 m length). The catalyst was exposed at a pressure of about 20 bar to a feed of 48 g/hour of methanol, 8.2 g/hour of hydrogen peroxide (40% by weight) and 4.7 g/hour of propylene (96% by volume of propylene). Temperatures were regulated between 20 and 40° C.

The analysis of the product mixture emerging from the reactor resulted in that after 230 hours, the selectivity for propylene oxide (with respect to H₂O₂) was 91%. The formation of oxygen (selectivity with respect to H₂O₂) was measured to be 2.4% and the unwanted side product methoxy propanol was formed with a selectivity of 3.3%.

EXAMPLE 1 (CATALYST ACCORDING TO THE PRESENT INVENTION)

In a four neck flask, 613 g of tetraethoxysilane were mixed with a solution of 316 g of tetrapropylammoniumhydroxide (40% by weight, in water) and 523 g of deionized water.

Separately, 18.1 g of tetrabutylorthotitanate were dissolved in 109 g of propylene glycol until a clear solution forms.

Said solution was dosed dropwise into the mixture of tetraethoxysilane and tetrapropylammoniumhydroxide described above. The resulting solution was stirred for 30 minutes. Subsequently, the alcohol formed due to hydrolysis was distilled at a bottom temperature of 92° C. The bottom (953 g) was filled with water to 1600 g.

This batch was reacted in a steel autoclave at 175° C. and for 24 hours while being stirred. The cooled down mixture consisted of a white suspension. Therefrom, the solid material was filtrated, rinsed with water and dried at 120° C. for 24 hours. The yield of dried product was 209° C. Subsequently, said material was calcined in air twice for 5 hours, respectively, at a temperature of 450° C. The mass loss due to calcination was measured to be 13% by weight.

The content of Ti of the zeolite of MFI-structure thus obtained was 1.9% by weight.

The following test of the catalytic material as described above had been performed: In a pressure-tight glass reactor, 0.5 g of said catalyst was mixed with 45 ml of methanol. At a temperature of 0° C., 20 ml of propylene were dosed in and subsequently, by means of a pump, 18 g of hydrogen peroxide (30% by weight, in water; Merck) were metered in. After a reaction time of 5 hours, the mixture was expanded (pressure released) and the liquid phase was analyzed by means of gas chromatography. The reaction mixture contained 9.7% by weight of propylene oxide. Despite the lower content in Ti of the zeolite, the inventive catalyst was shown to be significantly more active than the respective catalyst from the comparative example C1.

EXAMPLE 2 (CATALYST ACCORDING TO THE PRESENT INVENTION)

The catalyst material as described in Example 1 was shaped into a shaped body according to the following procedure: 60 g of the inventive solid material as described in Example 1 were milled and mixed with the following substances: 56.5 g of silica sol (Ludox AS 40% by weight SiO₂), a total amount of 32.9 g of a polystyrene dispersion (43.5 weight % of polymer), 2.7 g of methyl cellulose (Walocel) and 0.88 g of polyethylene oxide (PEO). 20 g of water were added to the mass. Said mass was homogenized in a kneading apparatus.

However, the materials were not added at the same time. Specifically, during the process of kneading, the polystyrene dispersion was added within 5 minutes, and after 10 minutes the silica sol was added slowly. After 10 further minutes of kneading, the PEO was added and gobbled for a further 10 minutes. Subsequently, water was added in portions of 5 ml, respectively.

The paste so obtained was formed after a total of 60 minutes of kneading and at a extrusion pressure of 70 bar via an extruder having a matrix of 1.5 mm holes. This way the solid material was alternately formed into strands.

The shaped body contained this way was dried for 4 hours at 120° C. (heating ramp of 2 K per minute). Finally, the shaped body was calcined at 490° C. for 4 hours (heating ramp 1 K per minute). The atmosphere was air. The yield was 65.24 g. The content in titanium of the shaped body produced this way was 1.1% by weight.

Said shaped body was subjected to a long term test for selectivity: 13.5 g of the shaped bodies were loaded into a tube reactor (1.3 m length). The catalyst was exposed at a pressure of about 20 bar to a feed of 48 g/hour of methanol, 8.2 g/hour of hydrogen peroxide (40% by weight) and 4.7 g/hour of propylene (96% by volume of propylene). Temperatures were regulated between 20 and 40° C.

The analysis of the product mixture emerging from the reactor resulted in that after 215 hours, the selectivity for propylene oxide (with respect to H₂O₂) was 95.3%. The formation of oxygen (selectivity with respect to H₂O₂) was measured to be 0.6% and the unwanted side product methoxy propanol was formed with a selectivity of 2.4%.

Therefore, the catalyst of the invention not only showed increased activity over a catalyst which had not been subjected to the inventive partial step, but was otherwise obtained the same way, but also showed improved selectivity. 

1-19. (canceled)
 20. A process for preparing a solid material for use as catalytic material in an epoxidation reaction, the solid material comprising at least one zeolite and being at least partially crystalline, wherein a step (I) of an at least partial crystallization of at least one solid material comprising at least one zeolite out of a synthesis mixture involves at least one partial step of contacting at least one transition metal oxide source with at least one epoxide or hydrolysate thereof prior to or, during the at least partial crystallization of said synthesis mixture into said solid material, and wherein the at least one epoxide is the product of said epoxidation reaction.
 21. The process according to claim 20, wherein step (I) comprises at least the following partial steps (Ia) mixing at least one hydrolyzable silicon source with a mineralizing and/or structuring agent and water; (Ib) mixing at least one transition metal oxide source with an epoxide or a hydrolysate thereof; (Ic) mixing the mixtures from (Ia) and (Ib) so that at least a part of the hydrolyzable compounds hydrolyzes; (Id) distilling at least part of the alcohol that has been formed as a result of the at least partial hydrolisation of at least part of the hydrolyzable compounds; (Ie) adding water to the bottom of (Id); (If) reacting the synthesis mixture resulting from (Ie) at a temperature elevated with respect to room temperature.
 22. The process according to claim 21, wherein the hydrolyzable silicon source comprises at least one silicon oxide, the mineralizing and/or structuring agent comprises at least one tetraalkylammonium hydroxide, and the transition metal oxide source comprises at least one titanate.
 23. The process according to claim 22, wherein the hydrolyzable silicon source comprises at least tetraethoxy silicate, the mineralizing and/or structuring agent comprises at least tetrapropylammonium hydroxide, the transition metal oxide source comprises at least tetrabutylorthotitanate and the epoxide or the hydrolysate thereof comprises at least propylene oxide or propylene glycol.
 24. The process according to claim 20, wherein the at least one zeolite belongs to at least one of the following structure classes: MFI, MEL, MWW, BEA or any mixed structure thereof.
 25. The process according to claim 21, wherein the at least one zeolite belongs to at least one of the following structure classes: MFI, MEL, MWW, BEA or any mixed structure thereof.
 26. The process according to claim 20, step (1) of the at least partial crystallization resulting in a mixture (I) comprising at least said solid material and a mother liquor, said process further comprising the step (II) separating and/or concentrating the solid material in mixture (I).
 27. The process according to claim 21, step (I) of the at least partial crystallization resulting in a mixture (I) comprising at least said solid material and a mother liquor, said process further comprising the step (II) separating and/or concentrating the solid material in mixture (I).
 28. The process according to claim 26, wherein, after step (II), at least one of the following two additional steps is performed: (W) bringing the solid material from step (II) in contact with a composition containing water; (III) agglomerating or granulating or agglomerating and granulating the solid material from step (W) or from step (II).
 29. The process according to claim 27, wherein, after step (II), at least one of the following two additional steps is performed: (W) bringing the solid material from step (II) in contact with a composition containing water; (III) agglomerating or granulating or agglomerating and granulating the solid material from step (W) or from step (II).
 30. The process according to claim 28, wherein, after step (W), the solid material is separated from at least part of the composition containing water.
 31. The process according to claim 26, optionally comprising the step (III) agglomerating, or granulating, or agglomerating and granulating the solid material from step (II); said process further comprising the step (S) shaping the solid material from step (II) or (III) obtaining a shaped body.
 32. The process according to claim 31, wherein the following step (W) is performed after step (II), or after step (S), or after step (II) and after step (S) (W) bringing the solid material from step (II) or the shaped body from step (S) in contact with a composition containing water.
 33. The process according to claim 31, wherein step (S) is selected from the group consisting of pelletizing, pressing, extruding, sintering, roasting, and briquetting.
 34. Process according to claim 32, wherein step (S) is selected from the group consisting of pelletizing, pressing, extruding, sintering, roasting, and briquetting.
 35. Process according to claim 33, wherein before, or during, or before and during the step (S), a binding material is added to said solid material.
 36. Process according to claim 26, wherein after at least one of the steps (II), (W), (III) or (S), a step (C) of calcining the solid material, or the shaped body, or the solid material or the shaped body is performed.
 37. Process according to claim 36, wherein step (C) is performed at temperatures higher than 400° C.
 38. Process according to claim 26, wherein the process is an integrated process.
 39. A solid material comprising at least one zeolite for use as catalytic material in an epoxidation reaction, the solid material being obtainable by a process of treating a synthesis mixture, wherein a step (I) of an at least partial crystallization of at least one solid material comprising at least one zeolite out of a synthesis mixture involves at least one partial step of contacting at least one transition metal oxide source with at least one epoxide or hydrolysate thereof prior to or during the at least partial crystallization of said synthesis mixture into said solid material, and wherein the at least one epoxide is the product of said epoxidation reaction, said step (I) comprising at least the following partial steps (Ia) mixing at least one hydrolyzable silicon source with a mineralizing and/or structuring agent and water; (Ib) mixing at least one transition metal oxide source with an epoxide or a hydrolysate thereof; (Ic) mixing the mixtures from (Ia) and (Ib) so that at least a part of the hydrolyzable compounds hydrolyzes; (Id) distilling at least part of the alcohol that has been formed as a result of the at least partial hydrolisation of at least part of the hydrolyzable compounds; (Ie) adding water to the bottom of (Id); (If) reacting the synthesis mixture resulting from (Ie) at a temperature elevated with respect to room temperature.
 40. The solid material according to claim 39, wherein the solid material contains Ti.
 41. The solid material according to claim 39, wherein the solid material is shaped into a shaped body.
 42. A process for preparing a solid material for use as catalytic material in an epoxidation reaction, the solid material comprising at least one zeolite and being at least partially crystalline, wherein a step (I) of an at least partial crystallization of at least one solid material comprising at least one zeolite out of a synthesis mixture involves at least one partial step of contacting at least one transition metal oxide source with at least one epoxide or hydrolysate thereof prior to or during the at least partial crystallization of said synthesis mixture into said solid material, and wherein the at least one epoxide is the product of said epoxidation reaction, wherein step (I) comprises at least the following partial steps (Ia) mixing at least one hydrolyzable silicon source with a mineralizing and/or structuring agent and water; (Ib) mixing at least one transition metal oxide source with an epoxide or a hydrolysate thereof; (Ic) mixing the mixtures from (Ia) and (Ib) so that at least a part of the hydrolyzable compounds hydrolyzes; (Id) distilling at least part of the alcohol that has been formed as a result of the at least partial hydrolisation of at least part of the hydrolyzable compounds; (Ie) adding water to the bottom of (Id); (If) reacting the synthesis mixture resulting from (Ie) at a temperature elevated with respect to room temperature; wherein step (I) of the at least partial crystallization resulting in a mixture (I) comprising at least said solid material and a mother liquor, said process further comprising the step (II) separating and/or concentrating the solid material in mixture (I); optionally comprising the step (III) agglomerating, or granulating, or agglomerating and granulating the solid material from step (II); said process further comprising the step (S) shaping the solid material from step (II) or (III) obtaining a shaped body.
 43. A process for preparing a solid material for use as catalytic material in an epoxidation reaction, the solid material comprising at least one zeolite and being at least partially crystalline, wherein a step (1) of an at least partial crystallization of at least one solid material comprising at least one zeolite out of a synthesis mixture involves at least one partial step of contacting at least one transition metal oxide source with at least one epoxide or hydrolysate thereof prior to or during the at least partial crystallization of said synthesis mixture into said solid material, and wherein the at least one epoxide is the product of said epoxidation reaction, wherein step (I) comprises at least the following partial steps (Ia) mixing at least one hydrolyzable silicon source with a mineralizing and/or structuring agent and water; (Ib) mixing at least one transition metal oxide source with an epoxide or a hydrolysate thereof; (Ic) mixing the mixtures from (Ia) and (Ib) so that at least a part of the hydrolyzable compounds hydrolyzes; (Id) distilling at least part of the alcohol that has been formed as a result of the at least partial hydrolisation of at least part of the hydrolyzable compounds; (Ie) adding water to the bottom of (Id); (If) reacting the synthesis mixture resulting from (Ie) at a temperature elevated with respect to room temperature; wherein step (1) of the at least partial crystallization resulting in a mixture (I) comprising at least said solid material and a mother liquor, said process further comprising the step (II) separating and/or concentrating the solid material in mixture (I); optionally comprising the step (III) agglomerating, or granulating, or agglomerating and granulating the solid material from step (II); said process further comprising the step (S) shaping the solid material from step (II) or (III) obtaining a shaped body; and wherein the following step (W) is performed after step (II), or after step (S), or after step (II) and after step (S) (W) bringing the solid material from step (II) or the shaped body from step (S) in contact with a composition containing water. 